ZEDEX® 750 family

Cryogenics, high temp & high PV – up to 280 °C

ZX-750® family is suitable for very high temperatures, combined with high pv values. However, thanks to its low brittle point it can also be used in cryogenic applications.

ZX-750V5T® should always be used when the operating temperature exceeds 200°C and the loads, service life and dimensional stability have to be improved. ZX-750V5T® has the highest permissible surface pressure for speeds between 10 and 200 m/min and the best wear values at 150°C among the ZEDEX® materials.

The modification ZX-750V5KF® has almost the same aluminium CTE and its resilience values at -196°C are the 2nd best among the ZEDEX® materials, after ZX-324V11T®.

When to use the family ZX-750® ?

  • At very high temperatures
  • At very low temperatures
  • At very high pv values

When is the ZX-750® not suitable?

  • If low water absorption is required (e.g. the family ZX-530® as alternative)
  • If FDA conformity is required (e.g. the family ZX-530® as alternative)

What can be replaced?

WordPress Responsive Table

Basic type

ZX-750V5T

⟶ value the higher = better

ZX-750V5T Material data sheet

Characteristics

  • hard, stiff, tough
  • high dimensional stability
  • high fatigue strength
  • high weathering resistance
  • good fire behaviour (low generation of flue gases)
  • resistence to stress cracking
  • vacuum suitable
  • good machinability
  • bondable and weldable
  • contains PTFE

 

Resistance

  • UV-radiation: (1000 hours Xenon DIN 53597)
    tensile strength: no alteration, elongation at break: –30 %
  • Gamma-radiation: limit absorbed dose 8000 kGy
  • Chemicals, resistant: solvent, dilute acids and alkalis
  • Chemicals, not resistant: strong acids and alkalis, oxidizing agents
  • Lubricants and fuels: resistant
  • Water: max. water absorption: 0,7 %, dimensional changes: 0,4 %, up to 120 °C resistant
  • Fire behaviour: oxygen index (LOI): 52 %, 
    classification: V-0 (UL94)

Operational parameters

  • Temperature (T):
    –250 °C to +300 °C (+320 °C)
  • Surface pressure (p):
    max. 41 (125) MPa
  • Sliding speed (v)
    max. 350 m /min
  • Fatigue(S)
    tensile fatigue strength at 20 °C and and 106 stress cycles,
    1 Hz = 35 MPa

Available as:

Modification

ZX-750V5KF

⟶ value the higher = better

ZX-750V5KF Material data sheet

Characteristics

  • high stiffness up to 250 °C,
  • high elongation at break and yield
  • low thermal elongation
  • impact resistant down to –196 °C

 

Operational parameters

  • Temperature (T):
    –250 °C to +280 °C (+320 °C)
  • Surface pressure (p):
    max. 41 (125) MPa
  • Sliding speed (v)
    max. 350 m /min
  • Fatigue(S)
    tensile fatigue strength at 20 °C and and 106 stress cycles,
    1 Hz = 55 MPa

Available as:

Product shapes, processing methods
and finished parts

Product shapes

Processing methods

  • CNC milling
  • CNC lathe
  • Conventional lathe
  • CNC automatic lathe
  • Grinding
  • Threads
  • Dressing – profiling
  • Sawing
  • Planing
  • Roughening of adhesive surfaces
  • Injection moulding
  • Welding
  • Coating – cladding
  • Labelling
  • Bonding
  • 3D printing

Finished parts

  • Precision bushings
  • Plain bearing bushes according to DIN
  • Sliding guides
  • Slideways
  • Gears
  • Track rollers
  • Spindle nuts
  • Seals
  • Scrapers
  • Gear racks
  • Toothed belt discs
  • Rudder bearings
  • Pump bearings

Documentation

Application flyer

Technical data sheets

ZX-750V5T (TDS)

ZX-750V5KF (TDS)

Safety data sheets